Materials:

Below you will find the characteristics of the materials used for 3D printing.

 

ABS Plus

Thermoplastic material used in FDM technology. It is characterized by good mechanical properties, which tolerate the test of time well. ABS Plus is suitable for elements with very complex shapes, works well with the support dissolving agent, which facilitates the production of models with difficult geometry. ABS Plus can be dyed to different colors (white, black, yellow, orange, ivory and many other custom ones).

 

Value

Unit

Standard

Tensile strength Rm

33

MPa

ASTM D638

Tensile strength when yielding is reached

8

MPa

ASTM D638

Elasticity

2,200

MPa

ASTM D638

Elongation when the yield limit is reached

2

%

ASTM D638

Elongation at breakage

6

%

ASTM D638

Bending strength

     

oś. XZ

58

MPa

ASTM D790

oś. ZX

35

MPa

ASTM D790

Stroke. Izoda (23°C)

106

J/m

ASTM D256

Thermal deformation at 1.82 MPa

82

°C

ASTM D648

Bending elasticity module (23°C)

     

oś. XZ

2100

MPa

ASTM D790

oś. ZX

1650

MPa

ASTM D790

Temperature zeszklenia

108

°C

DSC (SSYS)

PA2200 (PA12)

Material with balanced properties and very versatile application. It has high strength and stiffness and chemical resistance. Suitable for further mechanical processing. PA12 material is used in Incremental SLS printing technology and allows for high dimensional accuracy.

Apply:

  • Utility parts.
  • Medical devices.
  • Fully functional plastic elements of the highest quality.
  • Replacements for typical injection molded plastics.
  • Implementation of connections of moving elements.

 

   

Value

Unit

Standard

Stroke Izoda (23°C)

 

4.4

kJ/m²

ISO 180/1A

Hardness by. Shore D (15s)

 

75

-

ISO 868

Strength factor (Young Module)

 

1650

MPa

ISO 527-1/-2

Tensile strength

       
 

The. X

48

MPa

ISO 527-1/-2

 

If. The

48

MPa

ISO 527-1/-2

 

The. Z

42

MPa

ISO 527-1/-2

Elongation at breakage

       
 

The. X

18

%

ISO 527-1/-2

 

If. The

18

%

ISO 527-1/-2

 

The. Z

4

%

ISO 527-1/-2

Bending elasticity module (23°C)

 

1500

MPa

ISO 178

Impact rate by Charpy (23°C a sample with notch)

 

4.8

kJ/m²

ISO 179/1eA

Udarność wg. Charpy’ego

 

53

kJ/m²

ISO 179/1eU

Thermal properties:

       

Melting point (20°C/min)

 

176

°C

ISO 11357-1/-3

Softening temperature by. Vicata (50°C/h 50N)

 

163

°C

ISO 306

 

VERO MORE

Acrylic resin with high rigidity used in the production of prototype elements.

Colors: white, black

 

Value

Unit

Standard

Tensile strength

50-65

MPa

D-638-03

Elongation at breakage

10-25

%

D-638-05

Flexibility module

2000

MPa

D-638-04

Bending strength

75-110

MPa

D-790-03

Bending elasticity module

2200-3200

MPa

D-790-04

Deflection temperature under load 0.45 MPa (°C)

45-50

°C

D-648-06

Deflection temperature under load of 1.82 MPa (°C)

45-50

°C

D-648-07

Stroke Izoda (23°C)

20-30

J/m

D-256-06

Absorbcja wody

1,1 - 1,5

%

D-570-98 24hr

Tg (°C)

52 - 54

°C

DMA E

Hardness by. Shore D

83 - 86

scale D

scale D

Hardness by. Rockwell’a M

73 - 76

scale M

scale M

Hardened material density

1,17 - 1,18

g/cm3

ASTM D 792

Ash content

0,23 - 0,26

%

UPS281

Tango Black Plus

Rubber-likematerial, characterized by good elasticity. It is used as an element of soft coatings and surfaces; prototype seals, handles, hoses, footwear and other flexible products.

Colors: white, black

 

Value

Unit

Standard

Tensile strength

0,8 - 1,5

MPa

D-412

Elongation at breakage

170 - 220

%

D-412

Permanent deformation after compression

4 - 5

%

D-395

Hardness by. Shore A

26 - 28

J/m

D-2240

Breaking strength

2 - 4

kg/cm

D-624

Hardened material density

1,17 - 1,18

g/cm3

ASTM D 792

Social media

In a few words about what we do

We provide comprehensive scanning, reverse engineering, 3D printing and optical metrology services throughout Poland and the EU. Our location makes us particularly close to Krakow, Katowice and Rzeszów. Many years of experience in the automotive and foundry industry is our asset. 3D scanner - Evicscan  3D HD  Quadro,which we have, allows for very accurate measurements even in very difficult conditions.

Teresa i Tomasz Polewka - Mandi House s.c.
Ul. Jurajskie Wzgórze 38 
32-087 Bibice (Kraków)
NIP: PL 5130246860
Regon: 365486818

 

Company information

skanowanie 3D, pomiary 3D, inżynieria odwrotna
skanowanie 3d, pomiary 3D, inżynieria odwrotna

Privacy